High-resistivity Fecral Insulation Heating Wire
Description:
With the high quality iron chrome aluminum for matrix, by pre - oxidation technology
treatment of the surface insulation resistance then tightly wound forming.Thermal efficiency increased by more than 20%.
0Cr25Al5
Chemical Content(%)
Mechanical Properties
Feature:
With long service life.Heating up fast.High thermal efficiency.Temperature uniformity. Can use vertically. When being used in the rated voltage,there is no volatile matter.It i the ne environmental protection electric heating wire.And an alternative to the costly nichrome wire.Can be customized according to customer requirements



Usage:
It is widely used in industrial furnace, household electrical appliances, infrared heater, etc.
The key properties:
1.The thickness of surface insulation resistance to oxidation layer: 5-15 μ m.
2. Insulation resistance: multimeter detection infinity.
3.The voltage-endurance of insulating single layer is greater than the alternating voltage 60 ν without breakdown.
4. The use of voltage: 6-380 ν.
5. Using temperature: Maximum1200 ºC
6. Service life: not less than 6000 hours.
7.Thermal shock performance: Electric heating element can withstand the cold and hot impact 600-6000 times without deformation.
Description:
With the high quality iron chrome aluminum for matrix, by pre - oxidation technology
treatment of the surface insulation resistance then tightly wound forming.Thermal efficiency increased by more than 20%.
0Cr25Al5
Chemical Content(%)
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
Max0.06 | Max 0.025 | Max 0.025 | Max 0.70 | Max 1.0 | 23.0~26.0 | Max 0.60 | 4.5~6.5 | Bal. | - |
Mechanical Properties
Max Continuous Service Temp | 1250ºC |
Resisivity at 20ºC | 1.42±0.06 ohm mm2/m |
Density | 7.10 g/cm3 |
Thermal Conductivity | 46.1KJ/m·h·ºC |
Coefficient of Thermal Expansion | 16.0×10-6/ºC |
Melting Point | 1500ºC |
Tensile Strength | 637~784 Mpa |
Elongation | Min 12% |
Section Variation Shrink Rate | 65~75% |
Repeatedly Bend Frequency | Min 5 times |
Continuous Service Time | - |
Hardness | 200-260HB |
Micrographic Structure | Ferrite |
Magnetic Property | Magnetic |
With long service life.Heating up fast.High thermal efficiency.Temperature uniformity. Can use vertically. When being used in the rated voltage,there is no volatile matter.It i the ne environmental protection electric heating wire.And an alternative to the costly nichrome wire.Can be customized according to customer requirements




It is widely used in industrial furnace, household electrical appliances, infrared heater, etc.
The key properties:
1.The thickness of surface insulation resistance to oxidation layer: 5-15 μ m.
2. Insulation resistance: multimeter detection infinity.
3.The voltage-endurance of insulating single layer is greater than the alternating voltage 60 ν without breakdown.
4. The use of voltage: 6-380 ν.
5. Using temperature: Maximum1200 ºC
6. Service life: not less than 6000 hours.
7.Thermal shock performance: Electric heating element can withstand the cold and hot impact 600-6000 times without deformation.